HP2 Plaster

HP2 Plaster is a formulated plaster used to produce working moulds for the slip casting of tableware and sanitaryware
Benefits
For slip casting in ceramics
Good balance between mould life and abosprtion capablity
Fine Particle Size
HP2 Plaster is a formulated plaster used to produce working moulds for the slip casting of tableware and sanitaryware
For slip casting in ceramics
Good balance between mould life and abosprtion capablity
Fine Particle Size
Mechanical Properties | |
---|---|
Brinell Hardness (MPa) | 39 |
Dry compressive strength (Mpa) | 18 |
Pore Volume (%) | 34% |
Physical Properties | |
---|---|
Bulk density (compacted) kg / m³ | 1360 |
Loose bulk density (kg/m³) | 930 |
Particle Size (% weight retained) |
45% at 32 µm 28% at 63 µm 15% at 90 µm 4.5% at 150 µm |
Chemical Properties | |
---|---|
Chemical Composition | CaSO4.1/2H2O |
Colour | white |
Setting Parameters | |
---|---|
Final setting time (minutes) | 14 |
Initial setting time (minutes) | 10 |
Linear Expansion (%) | 0,24 |
Vicat Ring Fluidity (cm) | 19 |
Plaster to Water Ratio | |
---|---|
Plaster to Water Ratio (by weight) | 1.61:1 |
Water to plaster ratio ( by weight) | 62% |
The recommended mixing time is approx. 2 to 4 minutes, depending on batch size.The precise consistency to use will need to be adjusted to suit the individual application. Changes to plaster to water ratio will influence product performance particularly setting time, strength and permeability.Depending on quality and preparation, the clay has a varying tendency to stick to the mould. Therefore the pwr may be adjusted within the above ranges. Depending on the quantity, the tendency to stick increases as the pwr increases. When inserting on the press, the lowest ratio should be tested first, followed by increasing increments to determine the optimum ratio.
Packaging available : 25 kg
Shelf life : 6 months